- 熔体流动速率 [g/10min]: 1.4
- 密度 [g/cm3]: 0.89
- 缺口冲击强度: 4.43
- 拉伸强度 [MPa]: 8.1
- 弯曲强度 [MPa]: 7.45
- 弯曲模量 [MPa]: 0.200
- 脆化温度 [℃]: -80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.890 - 0.926 g/cc | 0.0322 - 0.0335 lb/in³ | Average value: 0.921 g/cc Grade Count:23 |
| Particle Size | 400 - 1200 µm | 400 - 1200 µm | Average value: 771 µm Grade Count:7 |
| Environmental Stress Crack Resistance | 1.00 - 1000 hour | 1.00 - 1000 hour | Average value: 177 hour Grade Count:6 |
| Melt Flow | 1.40 - 70.0 g/10 min | 1.40 - 70.0 g/10 min | Average value: 23.5 g/10 min Grade Count:28 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 41.0 - 51.0 | 41.0 - 51.0 | Average value: 46.2 Grade Count:15 |
| Tensile Strength, Ultimate | 7.45 - 21.0 MPa | 1080 - 3050 psi | Average value: 13.1 MPa Grade Count:7 |
| Tensile Strength, Yield | 8.10 - 23.0 MPa | 1170 - 3340 psi | Average value: 12.8 MPa Grade Count:10 |
| Elongation at Break | 40.0 - 800 % | 40.0 - 800 % | Average value: 328 % Grade Count:11 |
| Flexural Modulus | 0.200 - 0.480 GPa | 29.0 - 69.6 ksi | Average value: 0.287 GPa Grade Count:5 |
| Secant Modulus | 0.230 - 0.448 GPa | 33.4 - 65.0 ksi | Average value: 0.354 GPa Grade Count:5 |
| Izod Impact, Notched | 4.43 - 5.00 J/cm | 8.30 - 9.37 ft-lb/in | Average value: 4.81 J/cm Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 112 - 124 °C | 234 - 255 °F | Average value: 121 °C Grade Count:17 |
| Vicat Softening Point | 88.0 - 94.0 °C | 190 - 201 °F | Average value: 91.8 °C Grade Count:10 |
| Brittleness Temperature | -80.0 - -68.0 °C | -112 - -90.4 °F | Average value: -74.3 °C Grade Count:7 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 160 - 230 °C | 320 - 446 °F | Average value: 199 °C Grade Count:3 |