- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.913
- 拉伸强度 [MPa]: 10.0
- 弯曲强度 [MPa]: 17.0
- 弯曲模量 [MPa]: 0.245
- 热变形温度 [℃]: 49.0
- 脆化温度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.913 - 0.945 g/cc | 0.0330 - 0.0341 lb/in³ | Average value: 0.935 g/cc Grade Count:49 |
| Environmental Stress Crack Resistance | 24.0 - 1000 hour | 24.0 - 1000 hour | Average value: 522 hour Grade Count:32 |
| 28.0 - 400 hour @Temperature 50.0 - 50.0 °C | 28.0 - 400 hour @Temperature 122 - 122 °F | Average value: 263 hour Grade Count:5 | |
| 28.0 - 400 hour @Thickness 2.00 - 2.00 mm | 28.0 - 400 hour @Thickness 0.0787 - 0.0787 in | Average value: 263 hour Grade Count:5 | |
| Melt Flow | 1.00 - 10.4 g/10 min | 1.00 - 10.4 g/10 min | Average value: 5.04 g/10 min Grade Count:49 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 17.0 - 30.1 MPa | 2470 - 4370 psi | Average value: 24.5 MPa Grade Count:6 |
| Tensile Strength, Yield | 10.0 - 22.8 MPa | 1450 - 3300 psi | Average value: 17.9 MPa Grade Count:45 |
| Elongation at Break | 239 - 1000 % | 239 - 1000 % | Average value: 662 % Grade Count:19 |
| Elongation at Yield | 11.0 - 20.6 % | 11.0 - 20.6 % | Average value: 16.0 % Grade Count:31 |
| Flexural Modulus | 0.245 - 1.05 GPa | 35.5 - 152 ksi | Average value: 0.676 GPa Grade Count:43 |
| Dynatup @ -30°C | 61.0 - 81.3 J | 45.0 - 60.0 ft-lb | Average value: 71.2 J Grade Count:6 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 104 - 127 °C | 220 - 261 °F | Average value: 125 °C Grade Count:23 |
| Crystallization Temperature | 109 - 113 °C | 229 - 235 °F | Average value: 111 °C Grade Count:8 |
| Deflection Temperature at 0.46 MPa (66 psi) | 49.0 - 62.0 °C | 120 - 144 °F | Average value: 56.1 °C Grade Count:36 |
| Deflection Temperature at 1.8 MPa (264 psi) | 37.0 - 41.0 °C | 98.6 - 106 °F | Average value: 38.5 °C Grade Count:25 |
| Vicat Softening Point | 91.0 - 117 °C | 196 - 243 °F | Average value: 110 °C Grade Count:9 |
| Brittleness Temperature | -75.0 - -70.0 °C | -103 - -94.0 °F | Average value: -70.6 °C Grade Count:8 |
| Flammability, UL94 | V-2 | V-2 | Grade Count:3 |
| Oxygen Index | 26.0 % | 26.0 % | Average value: 26.0 % Grade Count:3 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 124 - 232 °C | 255 - 450 °F | Average value: 141 °C Grade Count:6 |