- 弯曲模量 [MPa]: 0.228
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.918 g/cc | 0.918 g/cc | ASTM D792 |
| Melt Index of Compound | 0.90 g/10 min | 0.90 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 33.1 MPa | 4800 psi | transverse direction; ASTM D882 |
| 45.5 MPa | 6600 psi | machine direction; ASTM D882 | |
| Elongation at Break | 675 % | 675 % | machine direction; ASTM D882 |
| 750 % | 750 % | 50 mm/min; ASTM D638 | |
| 965 % | 965 % | transverse direction; ASTM D882 | |
| Flexural Modulus | 0.228 GPa | 33.0 ksi | 1% secant-machine direction; ASTM D882 |
| 0.241 GPa | 35.0 ksi | secant-transverse direction; ASTM D882 | |
| 0.365 GPa | 53.0 ksi | tangent, 1.3 mm/min; ASTM D790 | |
| Tear Strength | 390 kN/m | 2230 pli | machine direction; ASTM D1922A |
| 650 kN/m | 3710 pli | transverse direction; ASTM D1922A | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 99.0 °C | 210 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 15 % | 15 % | ASTM D1003 |
| Gloss | 45 % | 45 % | 45°; ASTM D2457 |