- 熔体流动速率 [g/10min]: 0.35
- 密度 [g/cm3]: 0.91
- 脆化温度 [℃]: -70.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 - 0.942 g/cc | 0.0329 - 0.0340 lb/in³ | Average value: 0.920 g/cc Grade Count:83 |
| Thickness | 8.00 - 50.0 microns | 0.315 - 1.97 mil | Average value: 29.1 microns Grade Count:63 |
| Melt Flow | 0.350 - 4.80 g/10 min | 0.350 - 4.80 g/10 min | Average value: 1.27 g/10 min Grade Count:83 |
| Antiblock Level | 500 - 7000 ppm | 500 - 7000 ppm | Average value: 5900 ppm Grade Count:6 |
| Slip Level | 1500 ppm | 1500 ppm | Average value: 1500 ppm Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 7.40 - 17.0 MPa | 1070 - 2470 psi | Average value: 11.0 MPa Grade Count:48 |
| Film Tensile Strength at Yield, TD | 7.60 - 17.0 MPa | 1100 - 2470 psi | Average value: 11.4 MPa Grade Count:48 |
| Film Elongation at Break, MD | 380 - 1320 % | 380 - 1320 % | Average value: 587 % Grade Count:79 |
| Film Elongation at Break, TD | 580 - 1400 % | 580 - 1400 % | Average value: 778 % Grade Count:79 |
| Film Elongation at Yield, MD | 19.0 - 43.0 % | 19.0 - 43.0 % | Average value: 27.5 % Grade Count:4 |
| Film Elongation at Yield, TD | 12.0 - 36.0 % | 12.0 - 36.0 % | Average value: 18.8 % Grade Count:4 |
| Secant Modulus, MD | 0.117 - 0.420 GPa | 17.0 - 60.9 ksi | Average value: 0.218 GPa Grade Count:57 |
| Secant Modulus, TD | 0.130 - 0.450 GPa | 18.9 - 65.3 ksi | Average value: 0.253 GPa Grade Count:57 |
| Coefficient of Friction | 0.100 - 1.00 | 0.100 - 1.00 | Average value: 0.510 Grade Count:41 |
| Elmendorf Tear Strength MD | 20.0 - 465 g | 20.0 - 465 g | Average value: 257 g Grade Count:26 |
| Elmendorf Tear Strength TD | 30.0 - 920 g | 30.0 - 920 g | Average value: 643 g Grade Count:26 |
| Elmendorf Tear Strength, MD | 0.530 - 17.7 g/micron | 13.5 - 450 g/mil | Average value: 11.2 g/micron Grade Count:66 |
| Elmendorf Tear Strength, TD | 0.790 - 45.3 g/micron | 20.1 - 1150 g/mil | Average value: 26.6 g/micron Grade Count:66 |
| Dart Drop | 2.20 - 34.0 g/micron | 56.0 - 864 g/mil | Average value: 5.75 g/micron Grade Count:56 |
| Dart drop Test | 70.0 - 850 g | 0.154 - 1.87 lb | Average value: 230 g Grade Count:40 |
| Film Tensile Strength at Break, MD | 25.5 - 74.5 MPa | 3700 - 10800 psi | Average value: 44.6 MPa Grade Count:79 |
| Film Tensile Strength at Break, TD | 20.0 - 60.0 MPa | 2900 - 8700 psi | Average value: 35.4 MPa Grade Count:79 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 116 - 127 °C | 241 - 261 °F | Average value: 124 °C Grade Count:25 |
| Vicat Softening Point | 95.0 - 119 °C | 203 - 246 °F | Average value: 105 °C Grade Count:13 |
| Brittleness Temperature | -70.0 °C | -94.0 °F | Average value: -70.0 °C Grade Count:8 |
| Optical Properties | Metric | English | Comments |
| Haze | 1.00 - 88.0 % | 1.00 - 88.0 % | Average value: 12.9 % Grade Count:74 |
| Gloss | 9.00 - 150 % | 9.00 - 150 % | Average value: 70.4 % Grade Count:74 |
| Transmission, Visible | 90.0 % | 90.0 % | Average value: 90.0 % Grade Count:8 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 180 - 270 °C | 356 - 518 °F | Average value: 222 °C Grade Count:14 |
| Melt Temperature | 195 - 300 °C | 383 - 572 °F | Average value: 221 °C Grade Count:25 |
| Die Opening | 0.0640 - 0.280 cm | 0.0252 - 0.110 in | Average value: 0.0991 cm Grade Count:14 |
| Extruder Size | 6.35 cm | 2.50 in | Average value: 6.35 cm Grade Count:11 |
| Blow-up Ratio (BUR) | 1.50 - 4.50 | 1.50 - 4.50 | Average value: 2.63 Grade Count:12 |