- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.916
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.916 g/cc | 0.0331 lb/in³ | ASTM D1505 | ||
| Thickness | 38.0 microns | 1.50 mil | |||
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 1286 % | 1286 % | ASTM D882 | ||
| Film Elongation at Break, TD | 1584 % | 1584 % | ASTM D882 | ||
| Secant Modulus, MD | 0.178 GPa | 25.8 ksi | 1%; ASTM D882 | ||
| Secant Modulus, TD | 0.183 GPa | 26.5 ksi | 1%; ASTM D882 | ||
| Coefficient of Friction | 1.0 | 1.0 | ASTM D1894 | ||
| Elmendorf Tear Strength, MD | 5.10 g/micron | 130 g/mil | ASTM 1922 | ||
| Elmendorf Tear Strength, TD | 14.9 g/micron | 378 g/mil | ASTM 1922 | ||
| Dart Drop | 2.63 g/micron | 66.8 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 45.0 MPa | 6530 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 20.3 % | 20.3 % | ASTM D1003 | ||
| Gloss | 6.7 % | 6.7 % | 60° angle; ASTM D2457 | ||
| Descriptive Properties | |||||
| Minimum Recommended Thickness | 30 µm | ||||