- 熔体流动速率 [g/10min]: 0.7
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.921 g/cc | 0.921 g/cc | ASTM D1505/D792 |
| Thickness | 38.0 microns | 1.50 mil | |
| Melt Flow | 0.70 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.70 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 970 % | 970 % | ASTM D882 |
| Film Elongation at Break, TD | 1230 % | 1230 % | ASTM D882 |
| Elmendorf Tear Strength MD | 70 g | 70 g | gF; ASTM D1922 |
| Elmendorf Tear Strength TD | 390 g | 390 g | gF; ASTM D1922 |
| Dart drop Test | 130 g | 0.287 lb | gF/50%f; ASTM D1709 |
| Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 |
| 1% Secant Modulus, MD | 200 MPa | 29000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 220 MPa | 31900 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 9.0 % @Thickness 0.0380 mm | 9.0 % @Thickness 0.00150 in | ASTM D1003 |
| Gloss | 115 % @Thickness 0.0380 mm | 115 % @Thickness 0.00150 in | 60°; ASTM D2457 |