- 熔体流动速率 [g/10min]: 0.75
- 密度 [g/cm3]: 0.919
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | ASTM-D792 |
| Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.75 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 880 % | 880 % | ASTM-D882 |
| Film Elongation at Break, TD | 1150 % | 1150 % | ASTM-D882 |
| Elmendorf Tear Strength MD | 150 g | 150 g | ASTM-D1922 |
| Elmendorf Tear Strength TD | 430 g | 430 g | ASTM-D1922 |
| Elmendorf Tear Strength, MD | 6.00 g/micron | 152 g/mil | ASTM-D1922 |
| Elmendorf Tear Strength, TD | 17.2 g/micron | 437 g/mil | ASTM-D1922 |
| Dart Drop | 4.80 g/micron | 122 g/mil | ASTM-D1709 |
| Dart drop Test | 120 g | 0.265 lb | ASTM-D1709 |
| Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM-D882 |
| Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM-D882 |
| 1% Secant Modulus, MD | 170 MPa | 24700 psi | ASTM-D882 |
| 1% Secant Modulus, TD | 190 MPa | 27600 psi | ASTM-D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 7.0 % | 7.0 % | ASTM-D1003 |
| Gloss | 95 % | 95 % | Angle 60°; ASTM-D2457 |