- 熔体流动速率 [g/10min]: 0.75
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ASTM-D792 |
| Melt Flow | 0.75 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.75 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 900 % | 900 % | ASTM-D882 |
| Film Elongation at Break, TD | 1240 % | 1240 % | ASTM-D882 |
| Elmendorf Tear Strength MD | 260 g | 260 g | ASTM-D1922 |
| Elmendorf Tear Strength TD | 570 g | 570 g | ASTM-D1922 |
| Elmendorf Tear Strength, MD | 10.4 g/micron | 264 g/mil | ASTM-D1922 |
| Elmendorf Tear Strength, TD | 22.8 g/micron | 579 g/mil | ASTM-D1922 |
| Dart Drop | 7.60 g/micron | 193 g/mil | ASTM-D1709 |
| Dart drop Test | 190 g | 0.419 lb | ASTM-D1709 |
| Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM-D882 |
| Film Tensile Strength at Break, TD | 40.0 MPa | 5800 psi | ASTM-D882 |
| 1% Secant Modulus, MD | 180 MPa | 26100 psi | ASTM-D882 |
| 1% Secant Modulus, TD | 200 MPa | 29000 psi | ASTM-D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 14 % | 14 % | ASTM-D1003 |
| Gloss | 103 % | 103 % | Angle 60°; ASTM-D2457 |