Braskem ML4400N LLDPE Rotomolding Polyethylene

Braskem ML4400N LLDPE Rotomolding Polyethylene 物性表: Braskem ML4400N LLDPE Rotomolding Polyethylene物性表及特性介绍,Braskem ML4400N LLDPE Rotomolding Polyethylene注塑参数详情,如需Braskem ML4400N LLDPE Rotomolding Polyethylene下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 3.9
  • 密度 [g/cm3]: 0.939
  • 拉伸强度 [MPa]: 21.0
  • 弯曲模量 [MPa]: 670
  • 热变形温度 [℃]: 60.0
 
Physical PropertiesMetricEnglishComments
Density 0.939 g/cc0.0339 lb/in³ASTM-D1505
ESCR 100% Igepal® 300 hour
@Thickness 2.00 mm,
Temperature 50.0 °C
300 hour
@Thickness 0.0787 in,
Temperature 122 °F
0.3 mm notched-plaques; ASTM-D1693
ESCR 10% Igepal® 28 hour
@Thickness 2.00 mm,
Temperature 50.0 °C
28 hour
@Thickness 0.0787 in,
Temperature 122 °F
0.3 mm notched-plaques; ASTM-D1693
Melt Flow 3.9 g/10 min
@Load 2.16 kg,
Temperature 190 °C
3.9 g/10 min
@Load 4.76 lb,
Temperature 374 °F
ASTM-D1238
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 24.0 MPa3480 psiASTM-D638
Tensile Strength, Yield 21.0 MPa3050 psiASTM-D638
Elongation at Break >= 1000 %>= 1000 %ASTM-D638
Elongation at Yield 13 %13 %ASTM-D638
Flexural Modulus, 1% Secant 670 MPa97200 psiASTM-D790
Impact Test  57.0 J
@Thickness 3.17 mm,
Temperature -40.0 °C
42.0 ft-lb
@Thickness 0.125 in,
Temperature -40.0 °F
ARM
 120 J
@Thickness 6.34 mm,
Temperature -40.0 °C
88.5 ft-lb
@Thickness 0.250 in,
Temperature -40.0 °F
ARM
 
Thermal PropertiesMetricEnglishComments
Deflection Temperature at 0.46 MPa (66 psi) 60.0 °C140 °FASTM-D648
Deflection Temperature at 1.8 MPa (264 psi) 40.0 °C104 °FASTM-D648
 
Processing PropertiesMetricEnglishComments
Melt Temperature 126 °C259 °FASTM-D3418

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-39918.html

免责声明: 本文 Braskem ML4400N LLDPE Rotomolding Polyethylene 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4