- 熔体流动速率 [g/10min]: 0.65
- 密度 [g/cm3]: 0.925
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | ASTM-D792 |
| Melt Flow | 0.65 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.65 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 800 % | 800 % | ASTM-D882 |
| Film Elongation at Break, TD | 1130 % | 1130 % | ASTM-D882 |
| Elmendorf Tear Strength MD | 140 g | 140 g | ASTM-D1922 |
| Elmendorf Tear Strength TD | 460 g | 460 g | ASTM-D1922 |
| Elmendorf Tear Strength, MD | 5.60 g/micron | 142 g/mil | ASTM-D1922 |
| Elmendorf Tear Strength, TD | 18.4 g/micron | 467 g/mil | ASTM-D1922 |
| Dart Drop | 5.20 g/micron | 132 g/mil | ASTM-D1709 |
| Dart drop Test | 130 g | 0.287 lb | ASTM-D1709 |
| Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM-D882 |
| Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM-D882 |
| 1% Secant Modulus, MD | 230 MPa | 33400 psi | ASTM-D882 |
| 1% Secant Modulus, TD | 270 MPa | 39200 psi | ASTM-D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 8.0 % | 8.0 % | ASTM-D1003 |
| Gloss | 117 % | 117 % | Angle 60°; ASTM-D2457 |