- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | ASTM-D792 |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 1010 % | 1010 % | ASTM-D882 |
| Film Elongation at Break, TD | 1210 % | 1210 % | ASTM-D882 |
| Elmendorf Tear Strength MD | 230 g | 230 g | ASTM-D1922 |
| Elmendorf Tear Strength TD | 350 g | 350 g | ASTM-D1922 |
| Elmendorf Tear Strength, MD | 9.20 g/micron | 234 g/mil | ASTM-D1922 |
| Elmendorf Tear Strength, TD | 14.0 g/micron | 356 g/mil | ASTM-D1922 |
| Dart Drop | >= 34.0 g/micron | >= 864 g/mil | ASTM-D1709 |
| Dart drop Test | >= 850 g | >= 1.87 lb | ASTM-D1709 |
| Film Tensile Strength at Break, MD | 70.0 MPa | 10200 psi | ASTM-D882 |
| Film Tensile Strength at Break, TD | 60.0 MPa | 8700 psi | ASTM-D882 |
| 1% Secant Modulus, MD | 130 MPa | 18900 psi | ASTM-D882 |
| 1% Secant Modulus, TD | 150 MPa | 21800 psi | ASTM-D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 14 % | 14 % | ASTM-D1003 |
| Gloss | 81 % | 81 % | Angle 60°; ASTM-D2457 |