- 熔体流动速率 [g/10min]: 20.0
- 密度 [g/cm3]: 0.926
- 缺口冲击强度: 4.85
- 拉伸强度 [MPa]: 12.0
- 弯曲模量 [MPa]: 415
- 热变形温度 [℃]: 46.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in³ | ASTM-D1505 |
| ESCR 10% Igepal® | 1.5 hour @Thickness 2.00 mm, Temperature 50.0 °C | 1.5 hour @Thickness 0.0787 in, Temperature 122 °F | 0.3 mm notched-plaques; ASTM-D1693 |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 190 °C | 20 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 49 | 49 | ASTM-D2240 |
| Tensile Strength at Break | 11.0 MPa | 1600 psi | ASTM-D638 |
| Tensile Strength, Yield | 12.0 MPa | 1740 psi | ASTM-D638 |
| Elongation at Break | 340 % | 340 % | ASTM-D638 |
| Elongation at Yield | 16 % | 16 % | ASTM-D882 |
| Flexural Modulus, 1% Secant | 415 MPa | 60200 psi | ASTM-D790 |
| Izod Impact, Notched | 4.85 J/cm | 9.09 ft-lb/in | ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 46.0 °C | 115 °F | ASTM-D648 |
| Vicat Softening Point | 94.0 °C @Load 1.02 kg | 201 °F @Load 2.25 lb | ASTM-D1525 |