- 密度 [g/cm3]: 0.927
- 拉伸强度 [MPa]: 9.65
- 弯曲模量 [MPa]: 0.421
- 热变形温度 [℃]: 45.0
- 脆化温度 [℃]: -76.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.927 g/cc | 0.0335 lb/in³ | ASTM D792 |
| ESCR 100% Igepal® | 5.0 hour @Temperature 50.0 °C | 5.0 hour @Temperature 122 °F | F50; Molded and tested in accordance with ASTM D4976; ASTM D1693 |
| Melt Index of Compound | 55 g/10 min @Load 2.16 kg, Temperature 190 °C | 55 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 52 | 52 | Molded and tested in accordance with ASTM D4976; ASTM D2240 |
| Tensile Strength at Break | 7.58 MPa | 1100 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Tensile Strength, Yield | 9.65 MPa | 1400 psi | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Elongation at Break | 120 % | 120 % | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Elongation at Yield | 2.0 % | 2.0 % | Molded and tested in accordance with ASTM D4976; ASTM D638 |
| Flexural Modulus | 0.421 GPa | 61.0 ksi | 2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 B |
| Tensile Impact Strength | 189 kJ/m² | 90.0 ft-lb/in² | Molded and tested in accordance with ASTM D4976; ASTM D1822, Type S |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 124 °C | 255 °F | Dow Method (DSC) |
| Crystallization Temperature | 109 °C | 228 °F | Dow Method (DSC) |
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 °C | 113 °F | Molded and tested in accordance with ASTM D4976; ASTM D648 |
| Vicat Softening Point | 90.0 °C | 194 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.1 °C | <= -105 °F | Molded and tested in accordance with ASTM D4976; ASTM D746 |