- 熔体流动速率 [g/10min]: 0.5
- 密度 [g/cm3]: 0.9265
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.9265 g/cc | 0.03347 lb/in³ | ASTM D792 |
| Thickness | 19.0 microns | 0.750 mil | |
| Melt Flow | 0.50 g/10 min | 0.50 g/10 min | ASTM D1238 |
| Antiblock Level | 2500 ppm | 2500 ppm | |
| Slip Level | 650 ppm | 650 ppm | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 13.8 MPa | 2000 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 14.8 MPa | 2150 psi | ASTM D882 |
| Elmendorf Tear Strength MD | 170 g | 170 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 650 g | 650 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 8.92387 g/micron | 226.667 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 34.1207 g/micron | 866.667 g/mil | ASTM D1922 |
| Dart drop Test | 150 g | 0.331 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 58.6 MPa | 8500 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 40.0 MPa | 5800 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 122 °C | 252 °F | Dow Method (DSC) |
| Vicat Softening Point | 113 °C | 235 °F | ASTM D1525 |