- 熔体流动速率 [g/10min]: 0.85
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | ASTM D792 |
| Thickness | 20.3 microns | 0.800 mil | |
| Melt Flow | 0.85 g/10 min | 0.85 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 9.218 MPa | 1337 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 9.501 MPa | 1378 psi | ASTM D882 |
| Film Elongation at Break, MD | 421 % | 421 % | ASTM D882 |
| Film Elongation at Break, TD | 608 % | 608 % | ASTM D882 |
| Secant Modulus, MD | 0.149389 GPa | 21.6673 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.15536 GPa | 22.533 ksi | 2% Secant; ASTM D882 |
| Impact | 130 | 130 | [ft-lbf/in3]; Puncture Resistance; Dow Method |
| 765 | 765 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |
| 918 | 918 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| Elmendorf Tear Strength MD | 323 g | 323 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 518 g | 518 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 15.896 g/micron | 403.75 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 25.49 g/micron | 647.5 g/mil | ASTM D1922 |
| Dart drop Test | 474 g | 1.05 lb | Method A; ASTM D1709 |
| Film Tensile Strength at Break, MD | 33.34 MPa | 4835 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 25.66 MPa | 3722 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 122 °C | 252 °F | Dow Method (DSC) |
| Vicat Softening Point | 102 °C | 216 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 9.0 % | 9.0 % | ASTM D1003 |
| Gloss | 65 % | 65 % | 45°; ASTM D2457 |