- 熔体流动速率 [g/10min]: 3.2
- 密度 [g/cm3]: 0.919
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | ASTM D792 | ||
| Thickness | 20.3 microns | 0.800 mil | |||
| Melt Flow | 3.2 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.2 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 12.27 MPa | 1779 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 11.2 MPa | 1620 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 584 % | 584 % | ASTM D882 | ||
| Film Elongation at Break, TD | 875 % | 875 % | ASTM D882 | ||
| Elongation at Break | 363 % | 363 % | on-pallet testing: Ultimate Stretch; Highlight Industries, Inc. Method | ||
| Secant Modulus, MD | 0.149092 GPa | 21.6243 ksi | 2% Secant; ASTM D882 | ||
| Secant Modulus, TD | 0.158428 GPa | 22.9784 ksi | 2% Secant; ASTM D882 | ||
| Impact | 8.0 | 8.0 | [lbf]; Puncture Resistance Force; Dow Method | ||
| 272 | 272 | [ft-lbf/in3]; Puncture Resistance; Dow Method | |||
| Puncture Energy | 3.16 J | 2.33 ft-lb | Dow Method | ||
| Elmendorf Tear Strength MD | 164 g | 164 g | Method B; ASTM D1922 | ||
| Elmendorf Tear Strength TD | 567 g | 567 g | Method B; ASTM D1922 | ||
| Elmendorf Tear Strength, MD | 8.07 g/micron | 205 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 27.903 g/micron | 708.75 g/mil | ASTM D1922 | ||
| Dart drop Test | 96.0 g | 0.212 lb | Method A; ASTM D1709 | ||
| <= 100 g | <= 0.221 lb | Method B; ASTM D1709 | |||
| Film Tensile Strength at Break, MD | 60.17 MPa | 8727 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 40.77 MPa | 5913 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 123 °C | 253 °F | Dow Method (DSC) | ||
| Vicat Softening Point | 100 °C | 212 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 1.0 % | 1.0 % | ASTM D1003 | ||
| Gloss | 95 % | 95 % | 45°; ASTM D2457 | ||
| 157 % | 157 % | 20°; ASTM D2457 | |||
| Descriptive Properties | |||||
| Cling g | 208 | ASTM D5458, unstretched | |||