- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.92
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D792 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 10.28 MPa | 1491 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.03 MPa | 1455 psi | ASTM D882 |
| Film Elongation at Break, MD | 547 % | 547 % | ASTM D882 |
| Film Elongation at Break, TD | 654 % | 654 % | ASTM D882 |
| Secant Modulus, MD | 0.162041 GPa | 23.5024 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.195473 GPa | 28.3514 ksi | 2% Secant; ASTM D882 |
| Impact | 234 | 234 | [ft-lbf/in3]; Puncture Resistance; Dow Method |
| 1198 | 1198 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| 1302 | 1302 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |
| Elmendorf Tear Strength MD | 438 g | 438 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 690 g | 690 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 17.2 g/micron | 438 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 27.2 g/micron | 690 g/mil | ASTM D1922 |
| Dart drop Test | 232 g | 0.512 lb | Method A; ASTM D1709 |
| Film Tensile Strength at Break, MD | 50.34 MPa | 7301 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 36.02 MPa | 5224 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 121 °C | 250 °F | Dow Method (DSC) |
| Vicat Softening Point | 106 °C | 223 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 6.0 % | 6.0 % | ASTM D1003 |
| Gloss | 70 % | 70 % | 45°; ASTM D2457 |