- 熔体流动速率 [g/10min]: 2.3
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | ASTM D792 |
| Thickness | 58.4 microns | 2.30 mil | |
| Melt Flow | 2.3 g/10 min | 2.3 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 9.080 MPa | 1317 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 8.846 MPa | 1283 psi | ASTM D882 |
| Film Elongation at Break, MD | 432 % | 432 % | ASTM D882 |
| Film Elongation at Break, TD | 705 % | 705 % | ASTM D882 |
| Impact | 321 | 321 | [ft-lbf/in3]; Puncture Resistance; Dow Method |
| 2060 | 2060 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |
| 2653 | 2653 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| Elmendorf Tear Strength MD | 295 g | 295 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 558 g | 558 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 5.04963 g/micron | 128.261 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 9.55150 g/micron | 242.609 g/mil | ASTM D1922 |
| Dart drop Test | 148 g | 0.326 lb | Method B; ASTM D1709 |
| Film Tensile Strength at Break, MD | 50.11 MPa | 7268 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 35.9 MPa | 5210 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 123 °C | 253 °F | Dow Method (DSC) |
| Vicat Softening Point | 99.0 °C | 210 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 0.80 % | 0.80 % | ASTM D1003 |
| Gloss | 94.6 % | 94.6 % | 45°; ASTM D2457 |