- 熔体流动速率 [g/10min]: 3.2
- 密度 [g/cm3]: 0.919
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | ASTM D792 | ||
| Thickness | 50.8 microns | 2.00 mil | |||
| Melt Flow | 3.2 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.2 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 10.49 MPa | 1521 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 14.8 MPa | 2140 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 732 % | 732 % | ASTM D882 | ||
| Film Elongation at Break, TD | 608 % | 608 % | ASTM D882 | ||
| Elongation at Break | 574 % | 574 % | on-pallet testing: Ultimate Stretch; Highlight Industries, Inc. Method | ||
| Secant Modulus, MD | 0.155973 GPa | 22.6224 ksi | 2% Secant; ASTM D882 | ||
| Secant Modulus, TD | 0.154608 GPa | 22.4243 ksi | 2% Secant; ASTM D882 | ||
| Impact | 19 | 19 | [lbf]; Puncture Resistance Force; Dow Method | ||
| 264 | 264 | [ft-lbf/in3]; Puncture Resistance; Dow Method | |||
| Puncture Energy | 7.91 J | 5.83 ft-lb | Dow Method | ||
| Elmendorf Tear Strength MD | 758 g | 758 g | Method B; ASTM D1922 | ||
| Elmendorf Tear Strength TD | 979 g | 979 g | Method B; ASTM D1922 | ||
| Elmendorf Tear Strength, MD | 14.9 g/micron | 379 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 19.27 g/micron | 489.5 g/mil | ASTM D1922 | ||
| Dart drop Test | 126 g | 0.278 lb | Method B; ASTM D1709 | ||
| 332 g | 0.732 lb | Method A; ASTM D1709 | |||
| Film Tensile Strength at Break, MD | 40.62 MPa | 5892 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 56.3 MPa | 8170 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 123 °C | 253 °F | Dow Method (DSC) | ||
| Vicat Softening Point | 100 °C | 212 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 4.0 % | 4.0 % | ASTM D1003 | ||
| Gloss | 90 % | 90 % | 45°; ASTM D2457 | ||
| 143 % | 143 % | 20°; ASTM D2457 | |||
| Descriptive Properties | |||||
| Cling g | 242 | ASTM D5458, unstretched | |||