- 熔体流动速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.9255
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.9255 g/cc | 0.03344 lb/in³ | ASTM D792 |
| Thickness | 20.3 microns | 0.800 mil | |
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 16.28 MPa | 2361 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 19.73 MPa | 2862 psi | ASTM D882 |
| Film Elongation at Break, MD | 595 % | 595 % | ASTM D882 |
| Film Elongation at Break, TD | 727 % | 727 % | ASTM D882 |
| Secant Modulus, MD | 0.275577 GPa | 39.9696 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.332886 GPa | 48.2817 ksi | 2% Secant; ASTM D882 |
| Impact | 9.0 | 9.0 | [lbf]; Puncture Resistance Force; Dow Method |
| 172 | 172 | [ft-lbf/in3]; Puncture Resistance; Dow Method | |
| 3620 | 3620 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |
| 3881 | 3881 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| Puncture Energy | 2.37 J | 1.75 ft-lb | Dow Method |
| Elmendorf Tear Strength MD | 177 g | 177 g | Method B; ASTM D1922 |
| Elmendorf Tear Strength TD | 649 g | 649 g | Method B; ASTM D1922 |
| Elmendorf Tear Strength, MD | 8.7106 g/micron | 221.25 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 31.939 g/micron | 811.25 g/mil | ASTM D1922 |
| Dart drop Test | 58.0 g | 0.128 lb | Method A; ASTM D1709 |
| <= 100 g | <= 0.221 lb | Method B; ASTM D1709 | |
| Film Tensile Strength at Break, MD | 58.75 MPa | 8521 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 43.13 MPa | 6256 psi | ASTM D882 |
| Heat Seal Strength, Ultimate | 12.9 N | 2.90 lb (f) | at 160°C, 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method |
| Heat Seal Strength Initiation Temperature | 120 °C | 248 °F | 1 lb/in heat seal strength; 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 125 °C | 257 °F | Dow Method (DSC) |
| Vicat Softening Point | 113 °C | 235 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 9.0 % | 9.0 % | ASTM D1003 |
| Gloss | 56 % | 56 % | 45°; ASTM D2457 |
| 66 % | 66 % | 20°; ASTM D2457 | |