- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.9188
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.9188 g/cc | 0.03319 lb/in³ | ASTM D792 |
| Thickness | 50.8 microns | 2.00 mil | |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.80 MPa | 1711 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 14.42 MPa | 2091 psi | ASTM D882 |
| Film Elongation at Break, MD | 795 % | 795 % | ASTM D882 |
| Film Elongation at Break, TD | 820 % | 820 % | ASTM D882 |
| Secant Modulus, MD | 0.195715 GPa | 28.3864 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.218812 GPa | 31.7365 ksi | 2% Secant; ASTM D882 |
| Impact | 19 | 19 | [lbf]; Puncture Resistance Force; Dow Method |
| 216 | 216 | [ft-lbf/in3]; Puncture Resistance; Dow Method | |
| 3995 | 3995 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |
| 4359 | 4359 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| Puncture Energy | 6.78 J | 5.00 ft-lb | Dow Method |
| Elmendorf Tear Strength MD | 953 g | 953 g | Method B; ASTM D1922 |
| Elmendorf Tear Strength TD | 1294 g | 1294 g | Method B; ASTM D1922 |
| Elmendorf Tear Strength, MD | 18.76 g/micron | 476.5 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 25.5 g/micron | 647 g/mil | ASTM D1922 |
| Dart drop Test | 196 g | 0.432 lb | Method B; ASTM D1709 |
| 348 g | 0.767 lb | Method A; ASTM D1709 | |
| Film Tensile Strength at Break, MD | 54.24 MPa | 7867 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 53.63 MPa | 7778 psi | ASTM D882 |
| Heat Seal Strength, Ultimate | 20.5 N | 4.61 lb (f) | at 150°C, 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method |
| Heat Seal Strength Initiation Temperature | 120 °C | 248 °F | 1 lb/in heat seal strength; 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 124 °C | 255 °F | Dow Method (DSC) |
| Vicat Softening Point | 104 °C | 219 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 14 % | 14 % | ASTM D1003 |
| Gloss | 59 % | 59 % | 45°; ASTM D2457 |
| 64 % | 64 % | 20°; ASTM D2457 | |