- 熔体流动速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.9289
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.9289 g/cc | 0.03356 lb/in³ | ASTM D792 |
| Thickness | 20.3 microns | 0.800 mil | |
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Antiblock Level | 4000 ppm | 4000 ppm | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 16.62 MPa | 2411 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 19.59 MPa | 2841 psi | ASTM D882 |
| Film Elongation at Break, MD | 703 % | 703 % | ASTM D882 |
| Film Elongation at Break, TD | 793 % | 793 % | ASTM D882 |
| Secant Modulus, MD | 0.298577 GPa | 43.3057 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.282975 GPa | 41.0426 ksi | 2% Secant; ASTM D882 |
| Impact | 10 | 10 | [lbf]; Puncture Resistance Force; Dow Method |
| 101 | 101 | [ft-lbf/in3]; Puncture Resistance; Dow Method | |
| 3701 | 3701 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |
| 4832 | 4832 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| Puncture Energy | 2.15 J | 1.58 ft-lb | Dow Method |
| Elmendorf Tear Strength MD | 171 g | 171 g | Method B; ASTM D1922 |
| Elmendorf Tear Strength TD | 715 g | 715 g | Method B; ASTM D1922 |
| Elmendorf Tear Strength, MD | 8.4153 g/micron | 213.75 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 35.187 g/micron | 893.75 g/mil | ASTM D1922 |
| Dart drop Test | 55.0 g | 0.121 lb | Method A; ASTM D1709 |
| <= 100 g | <= 0.221 lb | Method B; ASTM D1709 | |
| Film Tensile Strength at Break, MD | 48.53 MPa | 7038 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 54.01 MPa | 7833 psi | ASTM D882 |
| Heat Seal Strength, Ultimate | 13.3 N | 2.99 lb (f) | at 140°C, 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method |
| Heat Seal Strength Initiation Temperature | 120 °C | 248 °F | 1 lb/in heat seal strength; 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 126 °C | 259 °F | Dow Method (DSC) |
| Vicat Softening Point | 116 °C | 241 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 9.0 % | 9.0 % | ASTM D1003 |
| Gloss | 73 % | 73 % | 45°; ASTM D2457 |
| 77 % | 77 % | 20°; ASTM D2457 | |