- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.9178
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.9178 g/cc | 0.03316 lb/in³ | ASTM D792 | ||
| Thickness | 20.3 microns | 0.800 mil | |||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 10.60 MPa | 1538 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 11.29 MPa | 1638 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 481 % | 481 % | ASTM D882 | ||
| Film Elongation at Break, TD | 891 % | 891 % | ASTM D882 | ||
| Elongation at Break | 295 % | 295 % | on-pallet testing: Ultimate Stretch; Highlight Industries, Inc. Method | ||
| Secant Modulus, MD | 0.142232 GPa | 20.6293 ksi | 2% Secant; ASTM D882 | ||
| Secant Modulus, TD | 0.150444 GPa | 21.8203 ksi | 2% Secant; ASTM D882 | ||
| Impact | 10 | 10 | [lbf]; Puncture Resistance Force; Dow Method | ||
| 372 | 372 | [ft-lbf/in3]; Puncture Resistance; Dow Method | |||
| 2453 | 2453 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |||
| 4321 | 4321 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |||
| Puncture Energy | 4.29 J | 3.17 ft-lb | Dow Method | ||
| Elmendorf Tear Strength MD | 224 g | 224 g | Method B; ASTM D1922 | ||
| Elmendorf Tear Strength TD | 640 g | 640 g | Method B; ASTM D1922 | ||
| Elmendorf Tear Strength, MD | 11.0 g/micron | 280 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 31.5 g/micron | 800 g/mil | ASTM D1922 | ||
| Dart drop Test | <= 100 g | <= 0.221 lb | Method B; ASTM D1709 | ||
| 134 g | 0.295 lb | Method A; ASTM D1709 | |||
| Film Tensile Strength at Break, MD | 55.66 MPa | 8073 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 47.22 MPa | 6849 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 123 °C | 253 °F | Dow Method (DSC) | ||
| Vicat Softening Point | 99.0 °C | 210 °F | ASTM D1525 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 1.0 % | 1.0 % | ASTM D1003 | ||
| Gloss | 95 % | 95 % | 45°; ASTM D2457 | ||
| 157 % | 157 % | 20°; ASTM D2457 | |||
| Descriptive Properties | |||||
| Cling g | 218 | ASTM D5458, unstretched | |||