- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.93
- 拉伸强度 [MPa]: 16.5
- 弯曲强度 [MPa]: 26.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | |
| Thickness | 40.0 microns | 1.57 mil | |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg | 1.0 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 8. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 26.2 MPa | 3800 psi | Molded property |
| Film Tensile Strength at Yield, MD | 14.5 MPa | 2100 psi | |
| Film Tensile Strength at Yield, TD | 17.2 MPa | 2490 psi | |
| Tensile Strength, Yield | 16.5 MPa | 2390 psi | Molded property |
| Film Elongation at Break, MD | 700 % | 700 % | |
| Film Elongation at Break, TD | 800 % | 800 % | |
| Elongation at Break | 900 % | 900 % | Molded value |
| Modulus of Elasticity | 0.413 GPa | 59.9 ksi | Molded Sample 2% Secant Modulus |
| Coefficient of Friction | 0.50 | 0.50 | |
| Elmendorf Tear Strength MD | 190 g | 190 g | |
| Elmendorf Tear Strength TD | 790 g | 790 g | |
| Elmendorf Tear Strength, MD | 4.80 g/micron | 122 g/mil | |
| Elmendorf Tear Strength, TD | 19.8 g/micron | 503 g/mil | |
| Dart Drop | 5.50 g/micron | 140 g/mil | |
| Film Tensile Strength at Break, MD | 43.4 MPa | 6290 psi | |
| Film Tensile Strength at Break, TD | 33.8 MPa | 4900 psi | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 112 °C | 234 °F | |
| Optical Properties | Metric | English | Comments |
| Haze | 12 % | 12 % | |
| Gloss | 47 % | 47 % | 45° |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 232 °C | 450 °F | Film extrusion temperature |