- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.922
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | |
| Thickness | 38.0 microns | 1.50 mil | |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg | 1.0 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 8.5. |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 12.0 MPa | 1740 psi | |
| Film Tensile Strength at Yield, TD | 12.0 MPa | 1740 psi | |
| Coefficient of Friction | 0.17 | 0.17 | |
| Elmendorf Tear Strength MD | 560 g | 560 g | |
| Elmendorf Tear Strength TD | 1050 g | 1050 g | |
| Elmendorf Tear Strength, MD | 14.7 g/micron | 373 g/mil | |
| Elmendorf Tear Strength, TD | 27.6 g/micron | 701 g/mil | |
| Dart Drop | 6.60 g/micron | 168 g/mil | |
| Film Tensile Strength at Break, MD | 36.0 MPa | 5220 psi | |
| Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 105 °C | 221 °F | |
| Optical Properties | Metric | English | Comments |
| Haze | 10 % | 10 % | |
| Gloss | 39 % | 39 % | 45° |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 226 °C | 439 °F | Film extrusion temperature |