- 熔体流动速率 [g/10min]: 0.95
- 密度 [g/cm3]: 0.92
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D792 |
| Melt Flow | 0.95 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.95 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 9.00 MPa | 1310 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Elongation at Break, MD | 675 % | 675 % | ASTM D882 |
| Film Elongation at Break, TD | 880 % | 880 % | ASTM D882 |
| Secant Modulus, MD | 0.176 GPa | 25.5 ksi | ASTM D882 |
| Secant Modulus, TD | 0.200 GPa | 29.0 ksi | ASTM D882 |
| Coefficient of Friction | 0.80 | 0.80 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 18.0 g/micron | 457 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 24.0 g/micron | 610 g/mil | ASTM D1922 |
| Dart Drop | 7.00 g/micron | 178 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 41.0 MPa | 5950 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 33.0 MPa | 4790 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 10 % @Thickness 0.0250 mm | 10 % @Thickness 0.000984 in | ASTM D1003 |
| Gloss | 58 % | 58 % | 45°; 1 mil; ASTM D1894 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 220 - 230 °C | 428 - 446 °F | |