- 熔体流动速率 [g/10min]: 0.95
- 密度 [g/cm3]: 0.924
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ASTM D792 |
| Moisture Vapor Transmission | 0.350 cc-mm/m²-24hr-atm | 0.889 cc-mil/100 in²-24hr-atm | or 14 g/m²-24 hr per 25 µm film; ASTM D1434 |
| Melt Flow | 0.95 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.95 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 58 | 58 | ASTM D2240 |
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 12.0 MPa | 1740 psi | ASTM D882 |
| Film Elongation at Break, MD | 720 % | 720 % | ASTM D882 |
| Film Elongation at Break, TD | 940 % | 940 % | ASTM D882 |
| Secant Modulus, MD | 0.218 GPa | 31.6 ksi | ASTM D882 |
| Secant Modulus, TD | 0.243 GPa | 35.2 ksi | ASTM D882 |
| Coefficient of Friction | >= 0.40 | >= 0.40 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 10.0 g/micron | 254 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 22.0 g/micron | 559 g/mil | ASTM D1922 |
| Dart Drop | 5.00 g/micron | 127 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 43.0 MPa | 6240 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 37.0 MPa | 5370 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 110 °C | 230 °F | ASTM D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D696 |
| Optical Properties | Metric | English | Comments |
| Haze | 8.0 % @Thickness 0.0250 mm | 8.0 % @Thickness 0.000984 in | ASTM D1003 |
| Gloss | 63 % | 63 % | 45°; 1 mil; ASTM D1894 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 210 - 220 °C | 410 - 428 °F | |