- 熔体流动速率 [g/10min]: 0.72
- 密度 [g/cm3]: 0.92
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D792 |
| Melt Flow | 0.72 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.72 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 9.00 MPa | 1310 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Elongation at Break, MD | 680 % | 680 % | ASTM D882 |
| Film Elongation at Break, TD | 975 % | 975 % | ASTM D882 |
| Secant Modulus, MD | 0.192 GPa | 27.8 ksi | ASTM D882 |
| Secant Modulus, TD | 0.200 GPa | 29.0 ksi | ASTM D882 |
| Coefficient of Friction | >= 1.0 | >= 1.0 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 24.0 g/micron | 610 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 26.0 g/micron | 660 g/mil | ASTM D1922 |
| Dart Drop | 8.40 g/micron | 213 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 48.0 MPa | 6960 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 46.1 MPa | 6690 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 10 % @Thickness 0.0250 mm | 10 % @Thickness 0.000984 in | ASTM D1003 |
| Gloss | 57 % | 57 % | 45°; 1 mil; ASTM D1894 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 220 - 230 °C | 428 - 446 °F | |