- 熔体流动速率 [g/10min]: 2.7
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D1505 | ||
| Thickness | 20.3 microns | 0.800 mil | |||
| Melt Flow | 2.7 g/10 min | 2.7 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 8.55 MPa | 1240 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 7.86 MPa | 1140 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 470 % | 470 % | ASTM D882 | ||
| Film Elongation at Break, TD | 720 % | 720 % | ASTM D882 | ||
| Puncture Energy | 4.18 J | 3.08 ft-lb | Exxon Mobil Method | ||
| Elmendorf Tear Strength MD | 170 g | 170 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 420 g | 420 g | ASTM D1922 | ||
| Elmendorf Tear Strength, MD | 8.366 g/micron | 212.5 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 20.7 g/micron | 525 g/mil | ASTM D1922 | ||
| Dart Drop | 8.366 g/micron | 212.5 g/mil | ASTM D1709 | ||
| Dart drop Test | 170 g | 0.375 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 75.08 MPa | 10890 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 51.4 MPa | 7450 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 109 MPa | 15800 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 132 MPa | 19100 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 117 °C | 243 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 1.8 % | 1.8 % | ASTM D1003 | ||
| Gloss | 91 % | 91 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||