- 熔体流动速率 [g/10min]: 5.2
- 密度 [g/cm3]: 0.932
- 拉伸强度 [MPa]: 15.2
- 弯曲模量 [MPa]: 0.600
- 热变形温度 [℃]: 55.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.932 g/cc | 0.0337 lb/in³ | ASTM D4883 | ||
| ESCR 100% Igepal® | >= 1000 hour | >= 1000 hour | ASTM D1693 | ||
| ESCR 10% Igepal® | 650 hour | 650 hour | ASTM D1693 | ||
| Melt Flow | 5.2 g/10 min @Load 2.16 kg, Temperature 190 °C | 5.2 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 15.2 MPa | 2200 psi | (2.0 in/min); ASTM D638 | ||
| Elongation at Yield | 20 % | 20 % | (2.0 in/min); ASTM D638 | ||
| Flexural Modulus | 0.600 GPa | 87.0 ksi | 1% secant; ASTM D790 | ||
| Impact Test | 88.1 J @Thickness 3.17 mm, Temperature -40.0 °C | 65.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F | ARM | ||
| 217 J @Thickness 6.35 mm, Temperature -40.0 °C | 160 ft-lb @Thickness 0.250 in, Temperature -40.0 °F | ARM | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 125 °C | 257 °F | ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 55.0 °C | 131 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 37.0 °C | 98.6 °F | ASTM D648 | ||
| Descriptive Properties | |||||
| Features | long term UV 8 stabilization | ||||
| Form | PELLET | ||||