- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | ExxonMobil Method | ||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 7.93 MPa | 1150 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 7.38 MPa | 1070 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 440 % | 440 % | ASTM D882 | ||
| Film Elongation at Break, TD | 840 % | 840 % | ASTM D882 | ||
| Puncture Energy | 3.28 J | 2.42 ft-lb | ExxonMobil | ||
| Elmendorf Tear Strength, MD | 11.32 g/micron | 287.5 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 36.91 g/micron | 937.5 g/mil | ASTM D1922 | ||
| Dart Drop | 3.94 g/micron | 100 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 64.0 MPa | 9280 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 41.2 MPa | 5980 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 110 MPa | 15900 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 123 MPa | 17900 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 124 °C | 255 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Crystallization Temperature | 109 °C | 228 °F | ASTM D3418 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 1.6 % | 1.6 % | ASTM D1003 | ||
| Gloss | 91 % | 91 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.