- 熔体流动速率 [g/10min]: 3.3
- 密度 [g/cm3]: 0.938
- 拉伸强度 [MPa]: 17.75
- 弯曲模量 [MPa]: 0.772
- 热变形温度 [℃]: 62.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.938 g/cc | 0.0339 lb/in³ | ASTM D4883 |
| ESCR 100% Igepal® | >= 1000 hour | >= 1000 hour | ASTM D1693 |
| ESCR 10% Igepal® | 145 hour | 145 hour | ASTM D1693 |
| Melt Flow | 3.3 g/10 min | 3.3 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 17.75 MPa | 2575 psi | ASTM D638 |
| Elongation at Yield | 17.7 % | 17.7 % | ASTM D638 |
| Flexural Modulus | 0.772 GPa | 112 ksi | 1% secant; ASTM D790 |
| Impact Test | 94.9 J @Thickness 3.17 mm, Temperature -40.0 °C | 70.0 ft-lb @Thickness 0.125 in, Temperature -40.0 °F | ARM |
| 258 J @Thickness 6.35 mm, Temperature -40.0 °C | 190 ft-lb @Thickness 0.250 in, Temperature -40.0 °F | ARM | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 127 °C | 261 °F | ASTM D3418 |
| Crystallization Temperature | 112.7 °C | 234.9 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 62.0 °C | 144 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 39.0 °C | 102 °F | ASTM D648 |