- 熔体流动速率 [g/10min]: 22.0
- 密度 [g/cm3]: 0.924
- 拉伸强度 [MPa]: 12.0
- 弯曲强度 [MPa]: 20.0
- 弯曲模量 [MPa]: 0.335
- 脆化温度 [℃]: -68.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | Exxon Method |
| Environmental Stress Crack Resistance | 250 hour | 250 hour | F50, Igepal, Condition C; ASTM D-1693 |
| Melt Flow | 22 g/10 min | 22 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 45 | 45 | ASTM D2240 |
| Tensile Strength, Ultimate | 20.0 MPa | 2900 psi | ASTM D638 |
| Tensile Strength, Yield | 12.0 MPa | 1740 psi | ASTM D638 |
| Elongation at Break | 345 % | 345 % | |
| Flexural Modulus | 0.335 GPa | 48.6 ksi | ASTM D790 |
| Tensile Impact Strength | 84.0 kJ/m² | 40.0 ft-lb/in² | 23°C; ASTM D-1822 |
| Dart Drop, Total Energy | 29.0 J | 21.4 ft-lb | Temp @ -40°C; F50; ASTM D-3029 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 122 °C | 252 °F | Exxon Method |
| Brittleness Temperature | -68.0 °C | -90.4 °F | ASTM D746 |