- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | Exxon Method |
| Thickness | 30.5 microns | 1.20 mil | |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 9.65 MPa | 1400 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.3 MPa | 1490 psi | ASTM D882 |
| Film Elongation at Break, MD | 660 % | 660 % | ASTM D882 |
| Film Elongation at Break, TD | 720 % | 720 % | ASTM D882 |
| Secant Modulus, MD | 0.221 GPa | 32.1 ksi | ASTM D882 |
| Secant Modulus, TD | 0.234 GPa | 33.9 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 430 g | 430 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 740 g | 740 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 14.1 g/micron | 358 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 24.3 g/micron | 617 g/mil | ASTM D1922 |
| Dart Drop | 8.19 g/micron | 208 g/mil | F50; ASTM D1709 |
| Dart drop Test | 250 g | 0.551 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 52.6 MPa | 7630 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 42.6 MPa | 6180 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 125 °C | 257 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 16 % | 16 % | ASTM D1003 |
| Gloss | 50 % | 50 % | 45°, ASTM D-2457 |