- 熔体流动速率 [g/10min]: 10.7
- 密度 [g/cm3]: 0.95
- 拉伸强度 [MPa]: 19.0
- 弯曲强度 [MPa]: 11.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | ASTM D1505 |
| Viscosity | 66 cP @Shear Rate 5000 1/s, Temperature 230 °C | 66 cP @Shear Rate 5000 1/s, Temperature 446 °F | Apparent viscosity; ASTM D3835 |
| 144 cP @Shear Rate 1000 1/s, Temperature 230 °C | 144 cP @Shear Rate 1000 1/s, Temperature 446 °F | Apparent viscosity; ASTM D3835 | |
| 228 cP @Shear Rate 300 1/s, Temperature 230 °C | 228 cP @Shear Rate 300 1/s, Temperature 446 °F | Apparent viscosity; ASTM D3835 | |
| Melt Flow | 10.7 g/10 min | 10.7 g/10 min | Melt Flow Ratio (I10/I2) is 7.7; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 64 | 64 | ASTM D2240 |
| Tensile Strength, Ultimate | 11.0 MPa | 1600 psi | ASTM D638 |
| Tensile Strength, Yield | 19.0 MPa | 2760 psi | ASTM D638 |
| Elongation at Break | 200 % | 200 % | ASTM D638 |
| Modulus of Elasticity | 0.938 GPa | 136 ksi | ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 117 °C | 243 °F | ASTM D1525 |