- 熔体流动速率 [g/10min]: 24.0
- 密度 [g/cm3]: 0.918
- 拉伸强度 [MPa]: 9.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D1505 |
| Viscosity | 48 cP @Shear Rate 5000 1/s, Temperature 230 °C | 48 cP @Shear Rate 5000 1/s, Temperature 446 °F | Apparent viscosity; ASTM D3835 |
| 92 cP @Shear Rate 1000 1/s, Temperature 230 °C | 92 cP @Shear Rate 1000 1/s, Temperature 446 °F | Apparent viscosity; ASTM D3835 | |
| 135 cP @Shear Rate 300 1/s, Temperature 230 °C | 135 cP @Shear Rate 300 1/s, Temperature 446 °F | Apparent viscosity; ASTM D3835 | |
| Melt Flow | 24 g/10 min | 24 g/10 min | Melt Flow Ratio (I10/I2) is 7.3; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 52 | 52 | ASTM D2240 |
| Tensile Strength, Yield | 9.00 MPa | 1310 psi | ASTM D638 |
| Elongation at Break | >= 300 % | >= 300 % | ASTM D638 |
| Modulus of Elasticity | 0.248 GPa | 36.0 ksi | ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 86.0 °C | 187 °F | ASTM D1525 |