- 熔体流动速率 [g/10min]: 2.2
- 密度 [g/cm3]: 0.932
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.932 g/cc | 0.0337 lb/in³ | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 2.2 g/10 min | 2.2 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 490 % | 490 % | ASTM D882 |
| Film Elongation at Break, TD | >= 700 % | >= 700 % | ASTM D882 |
| Secant Modulus, MD | 0.255 GPa | 37.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.297 GPa | 43.1 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 58 g | 58 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 710 g | 710 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 2.28 g/micron | 58.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 28.0 g/micron | 710 g/mil | ASTM D1922 |
| Dart Drop | 3.54 g/micron | 90.0 g/mil | ASTM D1709 |
| Dart drop Test | 90.0 g | 0.198 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 46.0 MPa | 6670 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 21.0 MPa | 3050 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 2.2 % | 2.2 % | ASTM D1003 |
| Gloss | 90 % | 90 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |