- 熔体流动速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.919
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 - 0.921 g/cc | 0.0332 - 0.0333 lb/in³ | ASTM D792 |
| Melt Flow | 0.80 - 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 - 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ISO 1184 |
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ISO 1184 |
| Film Elongation at Break, MD | >= 630 % | >= 630 % | ISO 1184 |
| Film Elongation at Break, TD | 800 % | 800 % | ISO 1184 |
| Dart drop Test | 130 g | 0.287 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | >= 35.0 MPa | >= 5080 psi | ISO 1184 |
| Film Tensile Strength at Break, TD | 28.0 MPa | 4060 psi | ISO 1184 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | >= 97.0 °C | >= 207 °F | ASTM D1525 |