- 熔体流动速率 [g/10min]: 3.0
- 密度 [g/cm3]: 0.916
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.916 g/cc | 0.0331 lb/in³ | ASTM D1505 | ||
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 11.8 MPa | 1710 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 500 % | 500 % | ASTM D882 | ||
| Film Elongation at Break, TD | 800 % | 800 % | ASTM D882 | ||
| 2% Secant Modulus | 0.115 GPa | 16.7 ksi | TD; ASTM D882 | ||
| 0.115 GPa | 16.7 ksi | MD; ASTM D882 | |||
| Elmendorf Tear Strength MD | 60 g | 60 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 330 g | 330 g | ASTM D1922 | ||
| Dart drop Test | 65.0 g | 0.143 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 52.0 MPa | 7540 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 24.0 MPa | 3480 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 2.0 % | 2.0 % | ASTM D1003 | ||
| Gloss | 88 % | 88 % | ASTM D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 °C | 500 °F | |||
| Descriptive Properties | |||||
| Puncture Resistance, N | 14 | Montell | |||