- 熔体流动速率 [g/10min]: 0.6
- 密度 [g/cm3]: 0.912
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.912 g/cc | 0.0329 lb/in³ | ASTM D1505 |
| Melt Flow | 0.60 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.60 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.5 MPa | 1670 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.2 MPa | 1620 psi | ASTM D882 |
| Film Elongation at Break, MD | 600 % | 600 % | ASTM D882 |
| Film Elongation at Break, TD | 760 % | 760 % | ASTM D882 |
| 2% Secant Modulus | 0.170 GPa | 24.7 ksi | MD; ASTM D882 |
| 0.185 GPa | 26.8 ksi | TD; ASTM D882 | |
| Elmendorf Tear Strength MD | 220 g | 220 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 420 g | 420 g | ASTM D1922 |
| Dart drop Test | 175 g | 0.386 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 43.0 MPa | 6240 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 42 % | 42 % | ASTM D1003 |
| Gloss | 35 % | 35 % | ASTM D2457 |