- 熔体流动速率 [g/10min]: 0.9
- 密度 [g/cm3]: 0.924
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 - 0.928 g/cc | 0.0334 - 0.0335 lb/in³ | ASTM D1505 |
| Melt Flow | 0.90 - 1.1 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.90 - 1.1 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 12.0 MPa | 1740 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 13.0 MPa | 1890 psi | ASTM D882 |
| Film Elongation at Break, MD | 650 % | 650 % | ASTM D882 |
| Film Elongation at Break, TD | 850 % | 850 % | ASTM D882 |
| Dart drop Test | 90.0 g | 0.198 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 42.0 MPa | 6090 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 33.0 MPa | 4790 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 105 °C | 221 °F | ASTM D1525-75 |
| Optical Properties | Metric | English | Comments |
| Haze | 13 % | 13 % | ASTM D1003 A-61 |
| Gloss | 48 % | 48 % | PU Meter, 45°C Head; ASTM D2456-70 |