- 熔体流动速率 [g/10min]: 2.3
- 密度 [g/cm3]: 0.92
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ISO 1183 |
| Melt Flow | 2.3 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.3 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Elongation at Break, MD | 1000 % | 1000 % | ASTM D882 |
| Film Elongation at Break, TD | 1100 % | 1100 % | ASTM D882 |
| 2% Secant Modulus | 0.0800 GPa | 11.6 ksi | MD; ASTM D882 |
| 0.100 GPa | 14.5 ksi | TD; ASTM D882 | |
| Coefficient of Friction | 0.13 | 0.13 | ASTM D1894 |
| Elmendorf Tear Strength MD | 100 g | 100 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 300 g | 300 g | ASTM D1922 |
| Dart drop Test | 90.0 g | 0.198 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 100 °C | 212 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 12 % | 12 % | ASTM D1003 |
| Gloss | 30 % | 30 % | ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 123 °C | 253 °F | |
| Mold Temperature | 225 °C | 437 °F | |