- 熔体流动速率 [g/10min]: 1.7
- 密度 [g/cm3]: 0.916
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.916 g/cc | 0.0331 lb/in³ | ASTM D1505-98 |
| Melt Flow | 1.7 - 2.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.7 - 2.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238-00 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 9.80 MPa | 1420 psi | ASTM D882-02 |
| Film Tensile Strength at Yield, TD | 9.30 MPa | 1350 psi | ASTM D882-02 |
| Film Elongation at Break, MD | 800 % | 800 % | ASTM D882-02 |
| Film Elongation at Break, TD | 890 % | 890 % | ASTM D882-02 |
| Film Elongation at Yield, MD | 47 % | 47 % | ASTM D882-02 |
| Film Elongation at Yield, TD | 35 % | 35 % | ASTM D882-02 |
| Coefficient of Friction | >= 1.0 | >= 1.0 | ASTM D1894-99 |
| Dart drop Test | 160 g | 0.353 lb | ASTM D1709-98 |
| Film Tensile Strength at Break, MD | 39.0 MPa | 5660 psi | ASTM D882-02 |
| Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882-02 |
| Optical Properties | Metric | English | Comments |
| Haze | 3.1 % | 3.1 % | ASTM D1003A-00 |
| Gloss | 83 % | 83 % | ASTM D785-03 |