- 熔体流动速率 [g/10min]: 0.6
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | ASTM D1505-98 |
| Melt Flow | 0.60 - 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.60 - 0.90 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238-00 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 13.0 MPa | 1890 psi | ASTM D882-02 |
| Film Tensile Strength at Yield, TD | 13.0 MPa | 1890 psi | ASTM D882-02 |
| Film Elongation at Break, MD | 790 % | 790 % | ASTM D882-02 |
| Film Elongation at Break, TD | 880 % | 880 % | ASTM D882-02 |
| Film Elongation at Yield, MD | 19 % | 19 % | ASTM D882-02 |
| Film Elongation at Yield, TD | 13 % | 13 % | ASTM D882-02 |
| Coefficient of Friction | 0.80 | 0.80 | ASTM D1894-99 |
| Dart drop Test | 210 g | 0.463 lb | ASTM D1709-98 |
| Film Tensile Strength at Break, MD | 42.0 MPa | 6090 psi | ASTM D882-02 |
| Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ASTM D882-02 |
| Optical Properties | Metric | English | Comments |
| Haze | 25 % | 25 % | ASTM D1003A-00 |
| Gloss | 30 % | 30 % | ASTM D785-03 |