- 熔体流动速率 [g/10min]: 0.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.918 - 0.922 g/cc | 0.918 - 0.922 g/cc | ASTM D1505 |
| Melt Flow | 0.80 - 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 - 1.2 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 36.3 MPa | 5260 psi | 50 mm/min; ASTM D638 |
| Film Elongation at Break, MD | 680 % | 680 % | Ultimate; ASTM D882 |
| Film Elongation at Break, TD | 800 % | 800 % | Ultimate; ASTM D882 |
| Elongation at Break | 850 % | 850 % | 50mm/min, Ultimate; ASTM D638 |
| Elmendorf Tear Strength MD | 12 g | 12 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 25 g | 25 g | ASTM D1922 |
| Dart drop Test | 370 g | 0.816 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 47.1 MPa | 6830 psi | Ultimate; ASTM D882 |
| Film Tensile Strength at Break, TD | 44.1 MPa | 6400 psi | Ultimate; ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 103 °C | 217 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 10 % | 10 % | ASTM D1003 |
| Gloss | 92 % | 92 % | 45°; ASTM D2457 |