- 熔体流动速率 [g/10min]: 2.4
- 密度 [g/cm3]: 0.919
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | ASTM D1505-98 |
| Melt Flow | 2.4 - 3.2 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.4 - 3.2 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238-00 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ASTM D882-02 |
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | ASTM D882-02 |
| Film Elongation at Break, MD | 820 % | 820 % | ASTM D882-02 |
| Film Elongation at Break, TD | 940 % | 940 % | ASTM D882-02 |
| Film Elongation at Yield, MD | 42 % | 42 % | ASTM D882-02 |
| Film Elongation at Yield, TD | 34 % | 34 % | ASTM D882-02 |
| Coefficient of Friction | >= 1.0 | >= 1.0 | ASTM D1894-99 |
| Dart drop Test | 130 g | 0.287 lb | ASTM D1709-98 |
| Film Tensile Strength at Break, MD | 37.0 MPa | 5370 psi | ASTM D882-02 |
| Film Tensile Strength at Break, TD | 32.0 MPa | 4640 psi | ASTM D882-02 |
| Optical Properties | Metric | English | Comments |
| Haze | 3.0 % | 3.0 % | ASTM D1003A-00 |
| Gloss | 83 % | 83 % | ASTM D785-03 |