- 熔体流动速率 [g/10min]: 0.95
- 密度 [g/cm3]: 0.922
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in³ | ASTM D1505 |
| Melt Flow | 0.95 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.95 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 13.0 MPa | 1890 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 12.5 MPa | 1810 psi | ASTM D882 |
| Film Elongation at Break, MD | 680 % | 680 % | ASTM D882 |
| Film Elongation at Break, TD | 780 % | 780 % | ASTM D882 |
| 2% Secant Modulus | 0.200 GPa | 29.0 ksi | MD; ASTM D882 |
| 0.240 GPa | 34.8 ksi | TD; ASTM D882 | |
| Elmendorf Tear Strength MD | 105 g | 105 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 460 g | 460 g | ASTM D1922 |
| Dart drop Test | 80.0 g | 0.176 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 45.0 MPa | 6530 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 21 % | 21 % | ASTM D1003 |
| Gloss | 38 % | 38 % | ASTM D2457 |