- 密度 [g/cm3]: 0.921
- 弯曲模量 [MPa]: 0.290
- 脆化温度 [℃]: -75.0
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 0.921 g/cc | 0.0333 lb/in³ | ASTM D792 |
High Load Melt Index | 12.7 g/10 min @Load 21.6 kg, Temperature 190 °C | 12.7 g/10 min @Load 47.6 lb, Temperature 374 °F | ASTM D1238 |
Melt Index of Compound | 0.24 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.24 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
0.24 g/10 min @Load 10.0 kg, Temperature 190 °C | 0.24 g/10 min @Load 22.0 lb, Temperature 374 °F | ASTM D1238 | |
Mechanical Properties | Metric | English | Comments |
Tensile Strength at Break | 18.1 MPa | 2630 psi | ASTM D638 |
Elongation at Break | 340 % | 340 % | ASTM D638 |
Flexural Modulus | 0.290 GPa | 42.1 ksi | ASTM D790 |
Izod Impact, Notched | NB | NB | ASTM D256 |
NB @Temperature -40.0 °C | NB @Temperature -40.0 °F | ASTM D256 | |
Thermal Properties | Metric | English | Comments |
Brittleness Temperature | <= -75.0 °C | <= -103 °F | ASTM D746 |