- 熔体流动速率 [g/10min]: 0.3
- 密度 [g/cm3]: 1.01
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | |||
| Thickness | 406 microns | 16.0 mil | |||
| Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.30 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 | ||
| 1.5 g/10 min @Load 5.00 kg, Temperature 190 °C | 1.5 g/10 min @Load 11.0 lb, Temperature 374 °F | ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 15.0 MPa | 2180 psi | ISO 527 | ||
| Film Tensile Strength at Yield, TD | 13.0 MPa | 1890 psi | ISO 527 | ||
| Film Elongation at Break, MD | 540 % | 540 % | ISO 527 | ||
| Film Elongation at Break, TD | 540 % | 540 % | ISO 527 | ||
| Film Elongation at Yield, MD | 15 % | 15 % | ISO 527 | ||
| Film Elongation at Yield, TD | 9.0 % | 9.0 % | ISO 527 | ||
| Film Tensile Strength at Break, MD | 22.0 MPa | 3190 psi | ISO 527 | ||
| Film Tensile Strength at Break, TD | 22.0 MPa | 3190 psi | ISO 527 | ||
| Electrical Properties | Metric | English | Comments | ||
| Surface Resistance | <= 100000 ohm | <= 100000 ohm | ISO D-257 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 160 - 200 °C | 320 - 392 °F | |||
| Blow-up Ratio (BUR) | >= 180 | >= 180 | |||
| Dry Time | 3 hour | 3 hour | At 90°C; If stored for longer than 1 year | ||
| Moisture Content | <= 0.15 % | <= 0.15 % | When Produced | ||
| Shelf Life | 12.0 Month | 12.0 Month | Normal Storing Conditions | ||
| Descriptive Properties | |||||
| Appearance | Granule | ||||
| Color | Black | ||||
| Screen Pack | As coarse as possible | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.