- 熔体流动速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | load density; ASTM D1505 |
| Thickness | 30.0 microns | 1.18 mil | |
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 12.0 MPa | 1740 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 13.0 MPa | 1890 psi | ASTM D882 |
| Film Elongation at Break, MD | 680 % | 680 % | ASTM D882 |
| Film Elongation at Break, TD | 850 % | 850 % | ASTM D882 |
| Elmendorf Tear Strength MD | 350 g | 350 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 550 g | 550 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 11.67 g/micron | 296.4 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 18.33 g/micron | 465.6 g/mil | ASTM D1922 |
| Dart drop Total Energy | 890 J/cm | 1.67 ft-lb/mil | Puncture Resistance; SABIC Method |
| Dart Drop | 5.00 g/micron | 127 g/mil | ASTM D1709 |
| Dart drop Test | 150 g | 0.331 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 48.0 MPa | 6960 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 40.0 MPa | 5800 psi | ASTM D882 |
| 1% Secant Modulus, MD | 280 MPa | 40600 psi | ASTM D882 |
| 1% Secant Modulus, TD | 300 MPa | 43500 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 101 °C | 214 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 12 % | 12 % | ASTM D1003 |
| Gloss | 80 % | 80 % | at 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 205 - 220 °C | 401 - 428 °F | |
| Blow-up Ratio (BUR) | 2.0 - 3.0 | 2.0 - 3.0 | |